Ruby Fused Alumina 80#-180#高鉻鉻剛玉研磨砂技術(shù)參數(shù)表

Ruby Fused Alumina 80#-180#高鉻鉻剛玉研磨砂

Ruby Fused Alumina 80#-180#高鉻鉻剛玉研磨砂的顏色比中鉻鉻剛玉的粉色更深。冶煉過(guò)程中添加的氧化鉻含量1-2%，其自銳性比棕剛玉高，韌性和耐磨性能比白剛玉高。氧化鉻的添加提高了剛玉的晶體的抗沖擊能力和機(jī)械強(qiáng)度，特別適合生產(chǎn)磨床砂輪、齒輪磨砂輪。針對(duì)淬火鋼高速鋼等材質(zhì)，其研磨效率比普通砂輪提高1-2倍，壽命提高4倍，大大提高了加工效率。

The color of Ruby fused alumina is darker than the pink fused alumina grain. The chromium oxide content added during the smelting process is 1-2%, and its self sharpening property is higher than that of brown fused alumina, and its toughness and wear resistance are higher than that of white fused alumina. The addition of chromium oxide improves the impact resistance and mechanical strength of corundum crystals, making it particularly suitable for producing grinding wheels and gear grinding wheels. For materials such as quenched steel and high-speed steel, the grinding efficiency is 1-2 times higher than that of ordinary grinding wheels, and the service life is increased by 4 times, greatly improving the processing efficiency.

Ruby Fused Alumina 80#-180#高鉻鉻剛玉研磨砂化學(xué)成分：

成分	F24～F80	F90～F150	F180～F220
AL₂O₃	≥97.4%	≥97%	≥96.5%
Cr₂O₃	1.0-2.0%	1.0-2.0%	1.0-2.0%
NA₂O	≤0.55%	≤0.60%	≤0.70%

Ruby Fused Alumina 80#-180#高鉻鉻剛玉研磨砂物理性能：

基本礦物	α-Al₂O₃
晶體尺寸	600-800 μm
莫氏硬度	9
努普硬度	2200-2300 kg/cm³
熔點(diǎn)	2050 ℃
比重	3.9-4.1g/cm³
堆積密度	1.40-1.91 g/cm³
顏色	粉色
晶型	多棱型

高鉻鉻剛玉的堆積密度如下：

粒度	堆積密度（g/cm3）
F24	1.69-1.79
F30	1.69-1.79
F36	1.68-1.79
F40	1.68-1.78
F46	1.68-1.79
F54	1.66-1.76
F60	1.65-1.75
F70	1.62-1.71
F80	1.58-1.68
F90	1.55-1.64
F100	1.51-1.62
F120	1.49-1.59
F150	1.46-1.55
F180	1.42-1.53
F220	1.38-1.47